Moldable Polyimide Film

JP Polyimide films for forming (e.g. kapton JP, JPB Film) have been designed to give optimum forming characteristics. The films for forming have higher elongations at elevated temperatures, enable drawing deeper parts at lower temperatures 280~300^oC.  and shorter cycle times. After forming, parts exhibit excellent shape retention and minimum shrinkage

Application:

1) Parts may be formed from Polyimide Films for Forming that were previously difficult or impossible to form with HN and VN:

2)  Diaphragms for automotive and heating and ventilating sensors and switches

3)  Speaker cones, domes, spiders, and surrounds

4)  Other applications including appliances, electronics, and aerospace

Technical Data:

    Appearance                                JP: transparent golden film, JPB: black film

    Nominal Thickness                           0.025, 0.050, 0.075, 0.100mm

    Width                                                    520 mm

    Tensile Strength                                     150 MPa

     Elongation                                                 40%

     Glass Transition Temperature(Tg)             260~285^oC

Core Size:  3" paper or plastic core

Special thickness or combinations can be supplied according to customer